Mechanical strength and corrosion detection of pozzolanic cement
Maha Rabea Abu-Serea; Hayam A. Mohamed;
Abstract
Various pozzolanic cement pastes based on ordinary Portland cement (OPC), granulated blast furnace slag (GBFS) and metakaolin (MK) were studied. Mixes were prepared using a water/solid ratio (W/S) of 0.25 wt.%. Hydration characteristics of the different hardened cement pastes were investigated via the examination of chemically-combined water content, compressive strength, and X-ray diffraction analysis under normal curing conditions at various time intervals up to 90 days. Thermal analysis (DTA/TGA) was carried out for the mix contains 30% Mk and GBFS at 28 days. The electrical conductivity was measured during the early stages of hydration for the various cement pastes at 30o C. Moreover, the corrosion potential of reinforced steel embedded in metakaolin - slag - cement system was studied in comparison to their corresponding ordinary Portland cement, to evaluate the probability of steel corrosion. The results showed that the values of Wn% in these blended pastes are higher than blended pastes with slag or metakaolin only. Also, mix containing 70% OPC, 15% Mk and 15% GBFS has higher compressive strength and corrosion resistance than the net cement paste. The results of thermal analysis indicate that the presence of 30% GBFS and MK consumed the CH formed as a result of the hydration of OPC (pozzolanic reaction).
Other data
Title | Mechanical strength and corrosion detection of pozzolanic cement | Authors | Maha Rabea Abu-Serea ; Hayam A. Mohamed | Keywords | Blended cement hydration;Electrical conductivity;Steel reinforcement;Corrosion detection | Issue Date | Aug-2013 | Journal | Housing and Building National Research Center Journal | Volume | 9 | Issue | 2 | Start page | 103 | End page | 108 | DOI | 10.1016/j.hbrcj.2013.05.005 |
Attached Files
File | Description | Size | Format | Existing users please Login |
---|---|---|---|---|
Paper 10.pdf | 784.82 kB | Adobe PDF | Request a copy |
Similar Items from Core Recommender Database
Items in Ain Shams Scholar are protected by copyright, with all rights reserved, unless otherwise indicated.