Effect of cyclic stress reduction on the high temperature creep characteristics of solid solution Al-2.9 wt% Mg alloy
Mahmoud, Moustafa;
Abstract
Creep characteristics of solid solution Al22?9 wt-%Mg alloy have been investigated under the effect of cyclic stress reduction of different amplitudes (12?47226?18 MPa) and frequencies (0?2020?44 Hz) at different working temperatures ranging from 533 to 593 K. It was found that increasing both amplitude and frequency of cyclic stress reduction resulted in an increase in both transient and steady state creep stages. The enhancement of creep rate was observed above either a threshold stress or a threshold frequency. The activation energy values of the mechanisms operating in both transient and steady state creep stages were found to be 130 and 171 kJ mol21 respectively.
Other data
Title | Effect of cyclic stress reduction on the high temperature creep characteristics of solid solution Al-2.9 wt% Mg alloy | Authors | Mahmoud, Moustafa | Keywords | Al–Mg alloys | Issue Date | 2011 | Publisher | Maney on behalf of the Institute | Journal | Materials Science and Technology | Volume | 27 | Issue | 1 | Start page | 44 | End page | 48 | DOI | 10.1179/174328409X453154 |
Recommend this item
Similar Items from Core Recommender Database
Items in Ain Shams Scholar are protected by copyright, with all rights reserved, unless otherwise indicated.